X22CrMoV12-1马氏体不锈钢高温形变热处理工艺探索研究
Research on High-temperature Thermomechanical Treatment Process of X22CrMoV12-1 Martensitic Stainless Steel
孙朝远,郭鸿镇,程立维,姚泽坤
点击:2618次 下载:0次
作者单位:西北工业大学材料学院
中文关键字:马氏体不锈钢;形变热处理;正交试验;力学性能
英文关键字:Martensitic stainless; Thermomechanical treatment; Orthogonal test; Mechanical properties
中文摘要:摘要:通过正交试验方法,探索了高温形变热处理新工艺对X22CrMoV12-1马氏体不锈钢锻件生产的可行性。研究结果表明:回火温度是影响这种不锈钢锻件强度和韧性的最显著因素,锻造温度为次要因素,变形量为最不显著因素;选定1075℃的锻造温度、40%的变形量,665℃的回火温度时,锻件能够很好地满足塑性标准要求,并可实现良好的强韧性匹配;高温形变热处理工艺锻后省去固溶工序处理,直接淬火后进行回火,可缩短产品的生产周期,降低生产的成本。
英文摘要:Abstract: The feasibility of high-temperature thermomechanical treatment process in X22CrMoV12-1 martensitic stainless steel forgings has been studied by orthogonal test method. The results show that: tempering temperature is the most significant factor, and the forging temperature is the secondary factor, while the deformation is the least significant factor;A good strength and impact toughness matched with proper plastic property of X22CrMoV12-1 martensitic stainless steel can be obtained by forging at 1075℃, 40% of deformation and tempering at 665℃; Forgings manufactured by high-temperature thermomechanical treatment method , direct quenching after forging without solution treatment, then tempering, which not only shorten the production cycle, but also reduce production costs.