加热温度对铜时效硬化钢表面氧化层结构和组成的影响
Effect of temperature on the structure and composition of surface oxidation layer of copper age-hardening steel
刘翊之，柴锋，杨才福，张永权，苏航
点击：2157次 下载：0次
作者单位：钢铁研究总院结构材料研究所
中文关键字：铜时效硬化钢；表面氧化；加热温度；富Cu-Ni相
英文关键字：high strength Cu-bearing steel; surface oxidation; temperature; Cu Ni-rich phase
中文摘要：本文应用扫描电镜背电子散射研究了加热温度对铜时效硬化钢HSLA-100表面氧化层结构和组成的影响。研究发现发现随加热温度提高对于氧化层厚度增加且结构发生变化,氧化层可根据其组成分为三个部分：氧化铁层、富Cu相层和过渡层。氧化层中的Cu以富Cu-Ni相的形式存在，加热温度对富Cu-Ni相的成分具有明显影响。且随加热温度提高，过渡层结构和组成均发生变化。
英文摘要：The effect of temperature on the structure and composition of surface oxidation layer of copper age-hardening steel was investigated using SEM BSE.The results showed that the thickness of oxidation layer increased and the structure changed as temperature raised.The whole oxidation layer can be divided to three parts:iron oxides layer,Cu-rich phase layer and interim layer.The Cu in the oxidation layer was in the form of Cu Ni-rich phase.As temperature raised, the structure and composition of interim layer changed.