Nb-7Ta合金再结晶退火温度研究
Study on Recrystallization Annealing Temperature of Nb-7Ta Alloy
冯 益, 徐铁伟, 李 芳, 付宝全
点击:3238次 下载:0次
作者单位:(西部超导材料科技有限公司, 陕西 西安 710016)
中文关键字:Nb-7Ta合金; 再结晶退火; 退火温度; 金相组织; 力学性能
英文关键字:Nb-7Ta alloy; recrystallization annealing; annealing temperature; microstructure; mechanical property
中文摘要:研究了退火温度对棒材组织、硬度及力学性能的影响,确定了变形量对铌钽合金棒再结晶退火温度的影响规律。结果表明,随变形量的增大,材料的再结晶退火温度降低。变形量为90%时,锻造棒材的再结晶退火温度为1000~1050 ℃;变形率95%时,轧制棒材的再结晶退火温度为950~1000 ℃。
英文摘要:The influences of recrystallization annealing temperature on microstructure, hardness and mechanical property of Nb-7Ta alloy were studied. The relation between deformation degree and recrystallization annealing temperature was determined. The results show that, the recrystallization annealing temperature decreases with the increase of deformation degree. The recrystallization annealing temperature of Nb-7Ta alloy bar is determined as follows:1000 ~1050 ℃ for forging (90%) rod and 950 ~1000 ℃ for rolling(95%) rod.