低碳Mn-Cr冷轧热镀锌双相钢的组织性能研究
Study on Properties and Microstructure of Low Carbon Mn-Cr Cold-rolled Galvanizing Dual Phase Steel
王科强, 刘仁东, 王 旭, 林 利
点击:3394次 下载:0次
作者单位:鞍钢股份有限公司 技术中心, 辽宁 鞍山 114009
中文关键字:组织; 力学性能; 热镀锌; 双相钢; 加热温度
英文关键字:microstructure; mechanical properties; hot galvanizing; dual phase steel; heating temperature
中文摘要:以低碳Mn-Cr冷轧热镀锌双相钢为对象,研究了两相区不同加热温度下钢的组织特征和力学性能。结果表明,钢的组织由铁素体和马氏体岛组成,马氏体岛在铁素体基体上均匀弥散分布,马氏体岛中有微孪晶存在,且在靠近马氏体岛相界的铁素体中存在非连续的(Fe,Cr,Mn)xCy析出物。随加热温度的升高,钢的屈服强度和伸长率明显升高,抗拉强度下降。
英文摘要:Low carbon Mn-Cr cold-rolled hot galvanizing dual phase steel was taken as an object of investigation, its microstructure characteristic and mechanical properties were studied at different heating temperature. The results show that the microstructure of the steel is composed of ferrite and martensite. Micro-twins exist in martensite and they distribute uniformly among ferrite base. Discontinuous (Fe, Cr, Mn)xCy exists in ferrite near martensite interface particularly. The yield strength and the elongation of the steel increase obviously and the tensile strength decreases with the increase of heating temperature.