提高厚斗齿铸件使用寿命的研究
Research on Improving Life of Heavy Section Tooth Casting
陈映川, 陆卫倩
点击:3057次 下载:0次
作者单位:(上海电机学院 机械工程学院, 上海 200240)
中文关键字:厚斗齿; 应力集中; 涂料处理; 齿尖快冷; 整体缓冷
英文关键字:heavy teeth concentration; stress; coating treatment; tooth tip fast-cooling; slow cooling
中文摘要:某铸造厂将挖掘机上斗齿的齿尖改为厚齿后发生断裂等早期失效。分析了厚斗齿可能失效的各种原因。 经研究发现,齿尖、齿腔厚薄尺寸相差较大引起的应力是断裂失效的主要原因, 并针对性的采取了一系列措施, 从根本上解决了早期失效的问题, 大大提高了厚斗齿铸件的使用寿命。
英文摘要:The early failure happened after changing teeth thickness of heavy hection hooth casting in a casting plant. The reasons for failure were analyzed. The main reason was the stress induced by difference of wall thickness. The early failure was resolved by adopting a series of measures. The life of the castings is greatly enhanced in actual production.