新型铜镍铝合金热处理工艺研究
Research on Heat Treatment Process for New Style CuNiAl Alloy
宋德军, 张 毅
点击:3130次 下载:0次
作者单位:(中国船舶重工集团公司 第七二五研究所, 河南 洛阳 471039)
中文关键字:铜镍铝合金; 热处理; 力学性能; K相
英文关键字:CuNiAl alloy; heat treatment process; mechanical property; K phase
中文摘要:对新型铜镍铝合金进行热处理工艺试验,通过金相、扫描电镜和力学性能测试等方法,研究热处理制度对其组织和力学性能的影响。结果表明:合金经(890±10) ℃保温30 min,出炉空冷到室温,其力学性能优良,组织以α相、KⅡ和 KⅣ相为主。
英文摘要:The heat treatment process for new style CuNiAl alloy was studied. The influences of heat treatment process on the microstructure and mechanical property were studied by metal microscope, TEM and mechanical property measurement. The results show that the alloy has good mechanical property after heat treating at 890 ℃ for 30 min then furnace cooling to room temperature, the α phase, KⅡ and KⅣ phase are dominate phases.