热处理对Mg-Sm变形镁合金组织与性能的影响
Influences of Heat Treatment on Microstructure and Properties of Mg-Sm Extruded Alloy
甄 睿1,2, 王章忠1, 孙扬善2, 杨 雪1
点击:3119次 下载:0次
作者单位:(1. 南京工程学院 材料工程学院, 江苏 南京 211167; 2. 东南大学 材料科学与工程学院, 江苏 南京 211189)
中文关键字:钐; 变形镁合金; 时效; 显微组织; 力学性能
英文关键字:Sm; extruded magnesium alloy; aging; microstructure; mechanical properties
中文摘要:采用拉伸、硬度、显微组织观察等方法,研究了热处理对挤压态Mg-Sm合金组织和力学性能的影响。结果表明,实验合金经T5处理后的硬度高于T6处理的,热处理后弥散析出的强化相提高了Mg-Sm合金的力学性能,尤其是提高了屈服强度。Mg-Sm合金T5处理峰时效时的σb达到217.4 MPa,σ0.2达到162.1 MPa,δ为13.1%。
英文摘要:The effects of heat treatment on the microstructure and mechanical properties of Mg-Sm extruded alloy were investigated by tensile test and hardness measurement. The results show that the hardness of the alloy after T5 treatment is higher than that after T6 treatment. After heat treatment, the mechanical properties, especially the yield strength of Mg-Sm alloy are improved by dispersedly separated strengthening phase. After T5 treatment, the tensile strength, yield strength and elongation of the Mg-Sm alloy reaches the peak 217.4 MPa, 162.1 MPa and 13.1%, respectively.