热处理对20钢TLP连接接头组织性能的影响
Effect of Heat Treatment on Microstructure and Properties of TLP Bonding Joint of 20 Steel
陈思杰, 王西涛
点击:3125次 下载:0次
作者单位:(河南理工大学 材料科学与工程学院, 河南 焦作 454000)
中文关键字:20钢; 瞬时液相扩散连接; 组织; 硬度;于热处理
英文关键字:20 steel; transient liquid-phase bonding; microstructures; hardness; heat treatment
中文摘要:用氩气保护,非晶箔 FeNiSiCrB 做中间层,对20钢进行了瞬时液相扩散连接试验,用显微镜观察了接头组织形貌,用显微硬度计测试了热处理前后接头的显微硬度。研究表明,热处理可以使接头组织均匀化,降低接头显微硬度,但热处理对接头中的脆性相没有明显影响。
英文摘要:20 steel pipes were joined by transient liquid-phase bonding process using FeNiSiCrB alloy as filler in argon atmosphere. The microstructure and hardness of the TLP bonding joint were observed and measured using SEM and hardmeter. The results show that the heat treatment can make joint microstructure homogeneous, and reduce the microhardness of joint. But there is no significant effect on the brittleness phase of joint by heat treatment.