复合管爆炸焊接装置中金刚砂填充物的试验研究
Experimental Research on Carborundum Stuffing in Explosive Welding Installation of Composite Tube
陆 明1, 庞敬军1, 戴 蒙2, 刘 鹏1
点击:4986次 下载:0次
作者单位:1.解放军理工大学 工程兵工程学院, 江苏 南京 210007; 2.总参第六十三研究所 科技处,江苏 南京 210007
中文关键字:爆炸焊接; 铝/不锈钢复合管; 模具; 金刚砂
英文关键字:explosive welding; Al/ stainless steel composite tube; mould; carborundum
中文摘要:采用金刚砂作为铝 / 不锈钢复合管爆炸焊接试验装置中的填充物,并在注水和不注水两种工艺下进行爆炸焊接试验。直观观测,因金刚砂注水后的密实度得到提高,因此复合管的变形量相对较小;采用扫描电镜和能谱仪从微观成分对两种工艺下制备的复合管界面进行比较,结果表明,金刚砂注水爆炸焊接的复合管,不仅其界面为规则的微、小波状结合,且产生的金属间化合物也更少;对注水工艺下制备的复合管结合界面进行力学性能检测,其力学性也完全满足使用要求。
英文摘要:Using carborundum as the stuffing of the explosive welding installation of Al/stainless steel composite tubes, the explosive welding experiments within two kinds of technology such as affusion and no-affusion were conducted. The carborundum became more close-grained after that it was affused with water, so the distortion of the composite tube became comparatively less. The interface of the composite tubes which were made in two kinds of technologies were analyzed by SEM and EDS. The results indicate that the composite tubes which made in the condition of carborundum affusion are only inerratic microwave form and small wave-form, but also have less intermetallic compound. The interface mechanical properties of the composite tubes which made in carborundum affusion were tested, the mechanical properties can completely satisfy the using requirement.